| Nguồn gốc: | China |
| Hàng hiệu: | HY |
| Chứng nhận: | ISO9001:2008 |
| Số lượng đặt hàng tối thiểu: | 1 tons |
|---|---|
| Giá bán: | Negotiation |
| chi tiết đóng gói: | Anti rust oil to be applied on material and each rod to be packed in paper sleeve |
| Thời gian giao hàng: | 30days |
| Điều khoản thanh toán: | T/T, L/C |
| Khả năng cung cấp: | 30tons a day |
| Product name: | Non-quenched and tempered rod | Surface condition: | Chrome plated |
|---|---|---|---|
| Chrome thickness: | 20 - 30 micron | Straightness: | Not more than 0.2MM/M |
| Tensile strength: | Not less than 750MPa | Yield strength: | Not less than 520 Mpa |
| Điểm nổi bật: | chrome plated piston rod,chrome plated steel rod |
||
ISO F7 Micro Alloy Steel Hydraulic Cylinder Rods Diameter 35-140 Mm Better Tensile Strength
Product Description
1. The directly turning non-quenched and tempered steel products are used for manufacturing injection
molding machine draglink, engineering machinery push rod and hydraulic prop with the feature that
hardened and tempered steel mechanical property needless quenched and tempered process.
2. Hardness: Hardness is more uniform on the whole cross section than quenched and tempered
42CrMo4, 40Cr and CK45
3. Turning performance: Turning performance is commensurate to 42CrMo4, 40Cr and CK45 or be
superior to them.
4. Save manufacturing expenses and avoid waste in the tempering process.
5. Shortened processing periods, enhance productivity and reduce the occupied capital.
6. Low processing cost, needless quenched and tempered process and the second turning
Detailed Description
1. MATERIAL: HY4700, HY4520
2. CHEMICAL COMPOSITION(%)
|
Material |
C% |
Mn% |
Si% |
S% |
P% |
V% |
Ni |
Cr% |
Mo |
Cu |
|
HY4700 |
0.38-0.45 |
1.20 ~1.60 |
0.30~0.50 |
≤0.035 |
≤0.020 |
0.05～0.15 |
≤0.25 |
0.10～0.20 |
≤0.15 |
0.25 |
|
HY4520 |
0.40 ~0.48 |
0.80 ~1.40 |
0.15 ~0.35 |
≤0.035 |
≤0.035 |
≤0.15 |
≤0.25 |
≤0.25 |
≤0.15 |
≤0.25 |
3. MECHANICAL PROPERTIES
|
Material |
MECHANICAL PROPERTIES |
Surface hardness(HBW) |
|||||
|
Rm(MPa) |
Rel(MPa) |
A% |
Z% |
KU2(J) |
|
||
|
HY4700 |
Φ35 - Φ100 |
900 - 1100 |
≥650 |
≥16 |
≥35 |
≥39 |
270-340 |
|
＞Φ100 - Φ140 |
850 - 950 |
≥600 |
≥16 |
≥35 |
≥39 |
270-340 |
|
|
HY4520 |
Φ40 - Φ100 |
750 - 900 |
≥520 |
≥19 |
≥40 |
≥39 |
230-290 |
|
＞Φ100～Φ140 |
750 - 900 |
≥520 |
≥17 |
≥35 |
≥39 |
230-290 |
|
|
|
|
|
|
|
|
|
|
4. SUPPLY CONDITION
Ground and chrome plated
5. CHROME THICKNESS
20 to 30 micron
6. SURFACE ROUGHNESS
Ra≤0.2 micron and Rt≤2 micron
7 .SURFACE HARDNESS
850-1150HV (vickers 100g)
8. STRAIGHTNESS
≤0.2MM/M
9. TOLERANCES ON DIA
ISO f7 on the diameter
10.OVALITY
Half of the tolerance ISO f7
11. CORROSION RESISTANCE
Test in natural salt spray according to ASTM B 117-120hours
Results evaluation according to ISO 4540 RATING 7-10
12. COHESION
No craks,breaking or detaching after thermic shock(warming up at 300 celsius degrees
and cooling in water)
13 .POROSITY
Test according to ISO 1456/1458 and result yaluation according to ISO 4540 rating 8-10
14. WELDABILITY
Good
15. PACKING
Anti rust oil to be applied on material and each rod to be packed in paper sleeve
16. CERTIFICATE
All certificate related with material heat treatment and plating is required
Người liên hệ: Miss. Patty
Tel: 8613921505262
Fax: 86-510-83952939